N07041 Nickel vs. EN 1.4655 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while EN 1.4655 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4655 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 23 to 25 |
| Fatigue Strength, MPa | 540 | |
| 320 |
| Shear Strength, MPa | 850 | |
| 460 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 720 to 730 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 450 to 480 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 150 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 510 to 580 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 26 |
| Strength to Weight: Bending, points | 34 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 4.0 |
| Thermal Shock Resistance, points | 38 | |
| 20 |