N07041 Nickel vs. EN 1.4938 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.4938 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4938 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
16 to 17
Fatigue Strength, MPa 540
390 to 520
Shear Strength, MPa 850
540 to 630
Tensile Strength: Ultimate (UTS), MPa 1400
870 to 1030
Tensile Strength: Yield (Proof), MPa 1050
640 to 870

Thermal Properties

Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
30
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
1050 to 1920
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
31 to 37
Strength to Weight: Bending, points 34
26 to 29
Thermal Diffusivity, mm2/s 3.0
8.1
Thermal Shock Resistance, points 38
30 to 35