N07041 Nickel vs. CC767S Brass
N07041 nickel belongs to the nickel alloys classification, while CC767S brass belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is CC767S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 14 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 150 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 11 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 100 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 47 | |
| 15 |
| Strength to Weight: Bending, points | 34 | |
| 16 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 34 |
| Thermal Shock Resistance, points | 38 | |
| 14 |