N07041 Nickel vs. Grade 350 Maraging Steel
N07041 nickel belongs to the nickel alloys classification, while grade 350 maraging steel belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is grade 350 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 4.1 to 18 |
| Shear Strength, MPa | 850 | |
| 710 to 1400 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 1140 to 2420 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 830 to 2300 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 98 to 190 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 38 to 82 |
| Strength to Weight: Bending, points | 34 | |
| 29 to 49 |
| Thermal Shock Resistance, points | 38 | |
| 35 to 74 |