N07041 Nickel vs. Grade 366 Molybdenum
N07041 nickel belongs to the nickel alloys classification, while grade 366 molybdenum belongs to the otherwise unclassified metals. There are 14 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is grade 366 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 300 |
| Elongation at Break, % | 14 | |
| 2.2 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 470 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 450 | |
| 210 |
| Thermal Expansion, µm/m-K | 12 | |
| 7.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 12 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 370 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 47 | |
| 13 |
| Strength to Weight: Bending, points | 34 | |
| 13 |
| Thermal Shock Resistance, points | 38 | |
| 18 |