N07041 Nickel vs. Nickel 200
Both N07041 nickel and nickel 200 are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is nickel 200.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 180 |
| Elongation at Break, % | 14 | |
| 23 to 44 |
| Fatigue Strength, MPa | 540 | |
| 120 to 350 |
| Shear Strength, MPa | 850 | |
| 300 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 420 to 540 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 120 to 370 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 450 |
| Thermal Conductivity, W/m-K | 11 | |
| 69 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 42 to 370 |
| Stiffness to Weight: Axial, points | 15 | |
| 11 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 47 | |
| 13 to 17 |
| Strength to Weight: Bending, points | 34 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 17 |
| Thermal Shock Resistance, points | 38 | |
| 13 to 16 |