N07041 Nickel vs. Nickel 600
Both N07041 nickel and nickel 600 are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is nickel 600.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 3.4 to 35 |
| Fatigue Strength, MPa | 540 | |
| 220 to 300 |
| Shear Strength, MPa | 850 | |
| 430 to 570 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 650 to 990 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 270 to 760 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Conductivity, W/m-K | 11 | |
| 14 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 31 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 190 to 1490 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 21 to 32 |
| Strength to Weight: Bending, points | 34 | |
| 20 to 26 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 3.6 |
| Thermal Shock Resistance, points | 38 | |
| 19 to 29 |