N07041 Nickel vs. SAE-AISI 1008 Steel
N07041 nickel belongs to the nickel alloys classification, while SAE-AISI 1008 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is SAE-AISI 1008 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 22 to 33 |
| Fatigue Strength, MPa | 540 | |
| 150 to 220 |
| Shear Strength, MPa | 850 | |
| 220 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 330 to 370 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 190 to 310 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 62 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 78 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 92 to 260 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 12 to 13 |
| Strength to Weight: Bending, points | 34 | |
| 13 to 15 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 17 |
| Thermal Shock Resistance, points | 38 | |
| 10 to 12 |