N07041 Nickel vs. SAE-AISI 1065 Steel

N07041 nickel belongs to the nickel alloys classification, while SAE-AISI 1065 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is SAE-AISI 1065 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 14
11 to 14
Fatigue Strength, MPa 540
270 to 340
Shear Strength, MPa 850
430 to 470
Tensile Strength: Ultimate (UTS), MPa 1400
710 to 780
Tensile Strength: Yield (Proof), MPa 1050
430 to 550

Thermal Properties

Melting Onset (Solidus), °C 1320
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
51
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
74 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
490 to 820
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 47
25 to 28
Strength to Weight: Bending, points 34
23 to 24
Thermal Diffusivity, mm2/s 3.0
14
Thermal Shock Resistance, points 38
25 to 27