N07041 Nickel vs. SAE-AISI 1548 Steel
N07041 nickel belongs to the nickel alloys classification, while SAE-AISI 1548 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is SAE-AISI 1548 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 | |
190 |
Elongation at Break, % | 14 | |
11 to 16 |
Fatigue Strength, MPa | 540 | |
270 to 430 |
Shear Strength, MPa | 850 | |
440 to 500 |
Tensile Strength: Ultimate (UTS), MPa | 1400 | |
730 to 830 |
Tensile Strength: Yield (Proof), MPa | 1050 | |
420 to 690 |
Thermal Properties
Melting Onset (Solidus), °C | 1320 | |
1420 |
Specific Heat Capacity, J/kg-K | 450 | |
470 |
Thermal Conductivity, W/m-K | 11 | |
51 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
79 to 99 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
470 to 1280 |
Stiffness to Weight: Axial, points | 15 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
24 |
Strength to Weight: Axial, points | 47 | |
26 to 30 |
Strength to Weight: Bending, points | 34 | |
23 to 25 |
Thermal Diffusivity, mm2/s | 3.0 | |
14 |
Thermal Shock Resistance, points | 38 | |
23 to 27 |