MakeItFrom.com
Menu (ESC)

N07041 Nickel vs. SAE-AISI D2 Steel

N07041 nickel belongs to the nickel alloys classification, while SAE-AISI D2 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is SAE-AISI D2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
190
Elongation at Break, % 14
5.0 to 16
Fatigue Strength, MPa 540
310 to 860
Shear Strength, MPa 850
460 to 1160
Tensile Strength: Ultimate (UTS), MPa 1400
760 to 2000
Tensile Strength: Yield (Proof), MPa 1050
470 to 1510

Thermal Properties

Melting Onset (Solidus), °C 1320
1390
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 11
31
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.7

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
92 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
570 to 5940
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
27 to 72
Strength to Weight: Bending, points 34
24 to 46
Thermal Diffusivity, mm2/s 3.0
8.3
Thermal Shock Resistance, points 38
25 to 67