N07041 Nickel vs. Titanium 6-6-2
N07041 nickel belongs to the nickel alloys classification, while titanium 6-6-2 belongs to the titanium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is titanium 6-6-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 6.7 to 9.0 |
| Fatigue Strength, MPa | 540 | |
| 590 to 670 |
| Shear Strength, MPa | 850 | |
| 670 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 1140 to 1370 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 1040 to 1230 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 540 |
| Thermal Conductivity, W/m-K | 11 | |
| 5.5 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.4 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 4.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 89 to 99 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 34 |
| Strength to Weight: Axial, points | 47 | |
| 66 to 79 |
| Strength to Weight: Bending, points | 34 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 2.1 |
| Thermal Shock Resistance, points | 38 | |
| 75 to 90 |