N07041 Nickel vs. Type 2 Magnetic Alloy
N07041 nickel belongs to the nickel alloys classification, while Type 2 magnetic alloy belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is Type 2 magnetic alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 2.0 to 38 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 510 to 910 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 260 to 870 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.4 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 18 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 170 to 2010 |
| Stiffness to Weight: Axial, points | 15 | |
| 12 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 17 to 30 |
| Strength to Weight: Bending, points | 34 | |
| 17 to 25 |
| Thermal Shock Resistance, points | 38 | |
| 16 to 29 |