N07041 Nickel vs. C43400 Brass
N07041 nickel belongs to the nickel alloys classification, while C43400 brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C43400 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 14 | |
| 3.0 to 49 |
| Shear Strength, MPa | 850 | |
| 250 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 310 to 690 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 110 to 560 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 380 |
| Thermal Conductivity, W/m-K | 11 | |
| 140 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.6 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 19 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 57 to 1420 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 34 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 41 |
| Thermal Shock Resistance, points | 38 | |
| 11 to 24 |