N07041 Nickel vs. C43500 Brass
N07041 nickel belongs to the nickel alloys classification, while C43500 brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C43500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 220 | |
110 |
Elongation at Break, % | 14 | |
8.5 to 46 |
Shear Strength, MPa | 850 | |
220 to 310 |
Tensile Strength: Ultimate (UTS), MPa | 1400 | |
320 to 530 |
Tensile Strength: Yield (Proof), MPa | 1050 | |
120 to 480 |
Thermal Properties
Melting Onset (Solidus), °C | 1320 | |
970 |
Specific Heat Capacity, J/kg-K | 450 | |
380 |
Thermal Conductivity, W/m-K | 11 | |
120 |
Thermal Expansion, µm/m-K | 12 | |
19 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.2 | |
8.5 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
44 to 120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
65 to 1040 |
Stiffness to Weight: Axial, points | 15 | |
7.2 |
Stiffness to Weight: Bending, points | 25 | |
19 |
Strength to Weight: Axial, points | 47 | |
10 to 17 |
Strength to Weight: Bending, points | 34 | |
12 to 17 |
Thermal Diffusivity, mm2/s | 3.0 | |
37 |
Thermal Shock Resistance, points | 38 | |
11 to 18 |