N07041 Nickel vs. C65500 Bronze
N07041 nickel belongs to the nickel alloys classification, while C65500 bronze belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C65500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 4.0 to 70 |
| Shear Strength, MPa | 850 | |
| 260 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 360 to 760 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 120 to 430 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 400 |
| Thermal Conductivity, W/m-K | 11 | |
| 36 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.6 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 11 to 450 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 62 to 790 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 12 to 24 |
| Strength to Weight: Bending, points | 34 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 10 |
| Thermal Shock Resistance, points | 38 | |
| 12 to 26 |