N07041 Nickel vs. C67500 Bronze
N07041 nickel belongs to the nickel alloys classification, while C67500 bronze belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C67500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 100 |
| Elongation at Break, % | 14 | |
| 14 to 33 |
| Shear Strength, MPa | 850 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 430 to 580 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 170 to 370 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 11 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 21 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 61 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 130 to 650 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 20 |
| Strength to Weight: Axial, points | 47 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 34 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 34 |
| Thermal Shock Resistance, points | 38 | |
| 14 to 19 |