N07041 Nickel vs. C68800 Brass
N07041 nickel belongs to the nickel alloys classification, while C68800 brass belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C68800 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Elongation at Break, % | 14 | |
| 2.0 to 36 |
| Shear Strength, MPa | 850 | |
| 380 to 510 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 570 to 890 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 390 to 790 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 950 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 400 |
| Thermal Conductivity, W/m-K | 11 | |
| 40 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 16 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 710 to 2860 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 19 to 30 |
| Strength to Weight: Bending, points | 34 | |
| 19 to 25 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 12 |
| Thermal Shock Resistance, points | 38 | |
| 19 to 30 |