N07041 Nickel vs. C74500 Nickel Silver
N07041 nickel belongs to the nickel alloys classification, while C74500 nickel silver belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C74500 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 3.0 to 24 |
| Shear Strength, MPa | 850 | |
| 310 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 390 to 700 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 380 to 600 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 11 | |
| 45 |
| Thermal Expansion, µm/m-K | 12 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.3 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 12 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 620 to 1540 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 13 to 23 |
| Strength to Weight: Bending, points | 34 | |
| 14 to 21 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 14 |
| Thermal Shock Resistance, points | 38 | |
| 13 to 23 |