N07041 Nickel vs. C75700 Nickel Silver
N07041 nickel belongs to the nickel alloys classification, while C75700 nickel silver belongs to the copper alloys. There are 18 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is C75700 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 14 | |
| 3.2 to 22 |
| Shear Strength, MPa | 850 | |
| 350 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 590 to 610 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 470 to 580 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 390 |
| Thermal Conductivity, W/m-K | 11 | |
| 40 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.4 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 19 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 930 to 1410 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 47 | |
| 19 to 20 |
| Strength to Weight: Bending, points | 34 | |
| 19 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 12 |
| Thermal Shock Resistance, points | 38 | |
| 22 to 23 |