N07041 Nickel vs. K93500 Alloy
N07041 nickel belongs to the nickel alloys classification, while K93500 alloy belongs to the iron alloys. There are 11 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is K93500 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 490 to 810 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 17 to 27 |
| Strength to Weight: Bending, points | 34 | |
| 17 to 23 |
| Thermal Shock Resistance, points | 38 | |
| 15 to 25 |