N07041 Nickel vs. N06230 Nickel
Both N07041 nickel and N06230 nickel are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 210 |
| Elongation at Break, % | 14 | |
| 38 to 48 |
| Fatigue Strength, MPa | 540 | |
| 250 to 360 |
| Shear Strength, MPa | 850 | |
| 420 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 620 to 840 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 330 to 400 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 420 |
| Thermal Conductivity, W/m-K | 11 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 9.5 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 200 to 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 250 to 380 |
| Stiffness to Weight: Axial, points | 15 | |
| 12 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 47 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 34 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 2.3 |
| Thermal Shock Resistance, points | 38 | |
| 17 to 23 |