N07041 Nickel vs. N08020 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while N08020 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is N08020 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 200 |
| Elongation at Break, % | 14 | |
| 15 to 34 |
| Fatigue Strength, MPa | 540 | |
| 210 to 240 |
| Shear Strength, MPa | 850 | |
| 380 to 410 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 610 to 620 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 270 to 420 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 460 |
| Thermal Conductivity, W/m-K | 11 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 83 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 180 to 440 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 21 |
| Strength to Weight: Bending, points | 34 | |
| 20 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 3.2 |
| Thermal Shock Resistance, points | 38 | |
| 15 |