N07041 Nickel vs. S33228 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while S33228 stainless steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is S33228 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
34
Fatigue Strength, MPa 540
170
Shear Strength, MPa 850
380
Tensile Strength: Ultimate (UTS), MPa 1400
570
Tensile Strength: Yield (Proof), MPa 1050
210

Thermal Properties

Melting Onset (Solidus), °C 1320
1360
Specific Heat Capacity, J/kg-K 450
470
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Density, g/cm3 8.2
8.0

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
150
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
110
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 47
20
Strength to Weight: Bending, points 34
19
Thermal Shock Resistance, points 38
13