N07041 Nickel vs. S66286 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while S66286 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is S66286 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 17 to 40 |
| Fatigue Strength, MPa | 540 | |
| 240 to 410 |
| Shear Strength, MPa | 850 | |
| 420 to 630 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 620 to 1020 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 280 to 670 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 150 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 190 to 1150 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 47 | |
| 22 to 36 |
| Strength to Weight: Bending, points | 34 | |
| 20 to 28 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 4.0 |
| Thermal Shock Resistance, points | 38 | |
| 13 to 22 |