N07041 Nickel vs. ZK61A Magnesium
N07041 nickel belongs to the nickel alloys classification, while ZK61A magnesium belongs to the magnesium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is N07041 nickel and the bottom bar is ZK61A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 46 |
| Elongation at Break, % | 14 | |
| 5.8 to 7.1 |
| Fatigue Strength, MPa | 540 | |
| 120 to 140 |
| Shear Strength, MPa | 850 | |
| 170 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 290 to 310 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 180 to 200 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 530 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 960 |
| Thermal Conductivity, W/m-K | 11 | |
| 120 |
| Thermal Expansion, µm/m-K | 12 | |
| 27 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 1.9 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 15 to 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 370 to 420 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 62 |
| Strength to Weight: Axial, points | 47 | |
| 42 to 45 |
| Strength to Weight: Bending, points | 34 | |
| 50 to 53 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 65 |
| Thermal Shock Resistance, points | 38 | |
| 17 to 18 |