N07041 Nickel vs. ZA-27
N07041 nickel belongs to the nickel alloys classification, while ZA-27 belongs to the zinc alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 78 |
| Elongation at Break, % | 14 | |
| 2.0 to 4.5 |
| Fatigue Strength, MPa | 540 | |
| 110 to 170 |
| Shear Strength, MPa | 850 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 400 to 430 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 260 to 370 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 530 |
| Thermal Conductivity, W/m-K | 11 | |
| 130 |
| Thermal Expansion, µm/m-K | 12 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 5.0 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 8.1 to 18 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 420 to 890 |
| Stiffness to Weight: Axial, points | 15 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 28 |
| Strength to Weight: Axial, points | 47 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 34 | |
| 24 to 25 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 47 |
| Thermal Shock Resistance, points | 38 | |
| 14 to 15 |