N07041 Nickel vs. ZA-8
N07041 nickel belongs to the nickel alloys classification, while ZA-8 belongs to the zinc alloys. There are 19 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 85 to 86 |
| Elongation at Break, % | 14 | |
| 1.3 to 8.0 |
| Fatigue Strength, MPa | 540 | |
| 51 to 100 |
| Shear Strength, MPa | 850 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 210 to 370 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 210 to 290 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 440 |
| Thermal Conductivity, W/m-K | 11 | |
| 120 |
| Thermal Expansion, µm/m-K | 12 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 6.3 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 2.8 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 47 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 34 | |
| 12 to 18 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 42 |
| Thermal Shock Resistance, points | 38 | |
| 7.6 to 13 |