MakeItFrom.com
Menu (ESC)

N08020 Stainless Steel vs. A356.0 Aluminum

N08020 stainless steel belongs to the iron alloys classification, while A356.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is N08020 stainless steel and the bottom bar is A356.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
70
Elongation at Break, % 15 to 34
3.0 to 6.0
Fatigue Strength, MPa 210 to 240
50 to 90
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
26
Tensile Strength: Ultimate (UTS), MPa 610 to 620
160 to 270
Tensile Strength: Yield (Proof), MPa 270 to 420
83 to 200

Thermal Properties

Latent Heat of Fusion, J/g 300
500
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1410
610
Melting Onset (Solidus), °C 1360
570
Specific Heat Capacity, J/kg-K 460
900
Thermal Conductivity, W/m-K 12
150
Thermal Expansion, µm/m-K 15
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
40
Electrical Conductivity: Equal Weight (Specific), % IACS 1.8
140

Otherwise Unclassified Properties

Base Metal Price, % relative 38
9.5
Density, g/cm3 8.2
2.6
Embodied Carbon, kg CO2/kg material 6.6
8.0
Embodied Energy, MJ/kg 92
150
Embodied Water, L/kg 220
1110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 170
4.8 to 15
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 440
49 to 300
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
53
Strength to Weight: Axial, points 21
17 to 29
Strength to Weight: Bending, points 20
25 to 36
Thermal Diffusivity, mm2/s 3.2
64
Thermal Shock Resistance, points 15
7.6 to 13

Alloy Composition

Aluminum (Al), % 0
91.1 to 93.3
Carbon (C), % 0 to 0.070
0
Chromium (Cr), % 19 to 21
0
Copper (Cu), % 3.0 to 4.0
0 to 0.2
Iron (Fe), % 29.9 to 44
0 to 0.2
Magnesium (Mg), % 0
0.25 to 0.45
Manganese (Mn), % 0 to 2.0
0 to 0.1
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 32 to 38
0
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
6.5 to 7.5
Sulfur (S), % 0 to 0.035
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.15