N08020 Stainless Steel vs. AISI 316 Stainless Steel
Both N08020 stainless steel and AISI 316 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N08020 stainless steel and the bottom bar is AISI 316 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 15 to 34 | |
| 8.0 to 55 |
| Fatigue Strength, MPa | 210 to 240 | |
| 210 to 430 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 78 |
| Shear Strength, MPa | 380 to 410 | |
| 350 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 620 | |
| 520 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 270 to 420 | |
| 230 to 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 290 |
| Maximum Temperature: Corrosion, °C | 490 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 590 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1400 |
| Melting Onset (Solidus), °C | 1360 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 15 |
| Thermal Expansion, µm/m-K | 15 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.6 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 19 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 6.6 | |
| 3.9 |
| Embodied Energy, MJ/kg | 92 | |
| 53 |
| Embodied Water, L/kg | 220 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 26 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 170 | |
| 85 to 260 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 440 | |
| 130 to 1820 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 18 to 41 |
| Strength to Weight: Bending, points | 20 | |
| 18 to 31 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 4.1 |
| Thermal Shock Resistance, points | 15 | |
| 11 to 26 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.080 |
| Chromium (Cr), % | 19 to 21 | |
| 16 to 18 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Iron (Fe), % | 29.9 to 44 | |
| 62 to 72 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 32 to 38 | |
| 10 to 14 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.030 |