N08028 Stainless Steel vs. EN 1.4597 Stainless Steel

Both N08028 stainless steel and EN 1.4597 stainless steel are iron alloys. They have 56% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08028 stainless steel and the bottom bar is EN 1.4597 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 45
45
Fatigue Strength, MPa 220
300
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 400
470
Tensile Strength: Ultimate (UTS), MPa 570
680
Tensile Strength: Yield (Proof), MPa 240
330

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Maximum Temperature: Corrosion, °C 460
410
Maximum Temperature: Mechanical, °C 1100
860
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1370
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 37
11
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.4
2.5
Embodied Energy, MJ/kg 89
36
Embodied Water, L/kg 240
140

Common Calculations

PREN (Pitting Resistance) 39
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
250
Resilience: Unit (Modulus of Resilience), kJ/m3 140
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
25
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 3.2
4.1
Thermal Shock Resistance, points 12
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 26 to 28
15 to 18
Copper (Cu), % 0.6 to 1.4
2.0 to 3.5
Iron (Fe), % 29 to 40.4
63 to 76.4
Manganese (Mn), % 0 to 2.5
6.5 to 9.0
Molybdenum (Mo), % 3.0 to 4.0
0 to 1.0
Nickel (Ni), % 30 to 34
0 to 3.0
Nitrogen (N), % 0
0.1 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.030