N08028 Stainless Steel vs. S44635 Stainless Steel

Both N08028 stainless steel and S44635 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08028 stainless steel and the bottom bar is S44635 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
240
Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 45
23
Fatigue Strength, MPa 220
390
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
81
Shear Strength, MPa 400
450
Tensile Strength: Ultimate (UTS), MPa 570
710
Tensile Strength: Yield (Proof), MPa 240
580

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Maximum Temperature: Corrosion, °C 460
610
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 16
11

Otherwise Unclassified Properties

Base Metal Price, % relative 37
22
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
4.4
Embodied Energy, MJ/kg 89
62
Embodied Water, L/kg 240
170

Common Calculations

PREN (Pitting Resistance) 39
39
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
150
Resilience: Unit (Modulus of Resilience), kJ/m3 140
810
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.2
4.4
Thermal Shock Resistance, points 12
23

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.025
Chromium (Cr), % 26 to 28
24.5 to 26
Copper (Cu), % 0.6 to 1.4
0
Iron (Fe), % 29 to 40.4
61.5 to 68.5
Manganese (Mn), % 0 to 2.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
3.5 to 4.5
Nickel (Ni), % 30 to 34
3.5 to 4.5
Niobium (Nb), % 0
0.2 to 0.8
Nitrogen (N), % 0
0 to 0.035
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
0.2 to 0.8