N08031 Stainless Steel vs. SAE-AISI 8660 Steel

Both N08031 stainless steel and SAE-AISI 8660 steel are iron alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08031 stainless steel and the bottom bar is SAE-AISI 8660 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
12
Fatigue Strength, MPa 290
340
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 81
73
Shear Strength, MPa 510
390
Tensile Strength: Ultimate (UTS), MPa 730
660
Tensile Strength: Yield (Proof), MPa 310
550

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 18
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.6
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 7.1
1.5
Embodied Energy, MJ/kg 96
20
Embodied Water, L/kg 240
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
73
Resilience: Unit (Modulus of Resilience), kJ/m3 230
800
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 3.1
10
Thermal Shock Resistance, points 14
19

Alloy Composition

Carbon (C), % 0 to 0.015
0.56 to 0.64
Chromium (Cr), % 26 to 28
0.4 to 0.6
Copper (Cu), % 1.0 to 1.4
0
Iron (Fe), % 29 to 36.9
96.4 to 97.6
Manganese (Mn), % 0 to 2.0
0.75 to 1.0
Molybdenum (Mo), % 6.0 to 7.0
0.15 to 0.25
Nickel (Ni), % 30 to 32
0.4 to 0.7
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.3
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040