N08120 Nickel vs. EN 1.1170 Steel
N08120 nickel belongs to the nickel alloys classification, while EN 1.1170 steel belongs to the iron alloys. They have a modest 33% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is N08120 nickel and the bottom bar is EN 1.1170 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 | |
| 16 to 17 |
| Fatigue Strength, MPa | 230 | |
| 220 to 330 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Shear Strength, MPa | 470 | |
| 390 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 700 | |
| 640 to 730 |
| Tensile Strength: Yield (Proof), MPa | 310 | |
| 330 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1000 | |
| 400 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 50 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 45 | |
| 2.1 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.2 | |
| 1.5 |
| Embodied Energy, MJ/kg | 100 | |
| 19 |
| Embodied Water, L/kg | 240 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 190 | |
| 91 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 | |
| 290 to 670 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 23 to 26 |
| Strength to Weight: Bending, points | 21 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 13 |
| Thermal Shock Resistance, points | 17 | |
| 20 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.4 | |
| 0 |
| Boron (B), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0.020 to 0.1 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 23 to 27 | |
| 0 to 0.4 |
| Cobalt (Co), % | 0 to 3.0 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 21 to 41.4 | |
| 96.7 to 98.5 |
| Manganese (Mn), % | 0 to 1.5 | |
| 1.3 to 1.7 |
| Molybdenum (Mo), % | 0 to 2.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 35 to 39 | |
| 0 to 0.4 |
| Niobium (Nb), % | 0.4 to 0.9 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.035 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Tungsten (W), % | 0 to 2.5 | |
| 0 |