N08221 Nickel vs. AWS E70C-B2L
N08221 nickel belongs to the nickel alloys classification, while AWS E70C-B2L belongs to the iron alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is N08221 nickel and the bottom bar is AWS E70C-B2L.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 | |
| 21 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 610 | |
| 580 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 260 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1390 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 44 | |
| 3.0 |
| Density, g/cm3 | 8.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 1.6 |
| Embodied Energy, MJ/kg | 110 | |
| 22 |
| Embodied Water, L/kg | 240 | |
| 54 |
Common Calculations
| PREN (Pitting Resistance) | 40 | |
| 3.0 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 20 |
| Strength to Weight: Bending, points | 19 | |
| 20 |
| Thermal Shock Resistance, points | 16 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.2 | |
| 0 |
| Carbon (C), % | 0 to 0.025 | |
| 0 to 0.050 |
| Chromium (Cr), % | 20 to 22 | |
| 1.0 to 1.5 |
| Copper (Cu), % | 1.5 to 3.0 | |
| 0 to 0.35 |
| Iron (Fe), % | 22 to 33.9 | |
| 95.1 to 98 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.4 to 1.0 |
| Molybdenum (Mo), % | 5.0 to 6.5 | |
| 0.4 to 0.65 |
| Nickel (Ni), % | 39 to 46 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.050 | |
| 0.25 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0.6 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 | |
| 0 to 0.5 |