N08221 Nickel vs. N07752 Nickel

Both N08221 nickel and N07752 nickel are nickel alloys. They have 67% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08221 nickel and the bottom bar is N07752 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
22
Fatigue Strength, MPa 190
450
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 410
710
Tensile Strength: Ultimate (UTS), MPa 610
1120
Tensile Strength: Yield (Proof), MPa 270
740

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Mechanical, °C 980
960
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1390
1330
Specific Heat Capacity, J/kg-K 460
460
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 44
60
Density, g/cm3 8.3
8.4
Embodied Carbon, kg CO2/kg material 7.9
10
Embodied Energy, MJ/kg 110
150
Embodied Water, L/kg 240
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
220
Resilience: Unit (Modulus of Resilience), kJ/m3 170
1450
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21
37
Strength to Weight: Bending, points 19
29
Thermal Shock Resistance, points 16
34

Alloy Composition

Aluminum (Al), % 0 to 0.2
0.4 to 1.0
Boron (B), % 0
0 to 0.0070
Carbon (C), % 0 to 0.025
0.020 to 0.060
Chromium (Cr), % 20 to 22
14.5 to 17
Cobalt (Co), % 0
0 to 0.050
Copper (Cu), % 1.5 to 3.0
0 to 0.5
Iron (Fe), % 22 to 33.9
5.0 to 9.0
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 5.0 to 6.5
0
Nickel (Ni), % 39 to 46
70 to 77.1
Niobium (Nb), % 0
0.7 to 1.2
Phosphorus (P), % 0
0 to 0.0080
Silicon (Si), % 0 to 0.050
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0030
Titanium (Ti), % 0.6 to 1.0
2.3 to 2.8
Vanadium (V), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.050