N08367 Stainless Steel vs. EN 1.0528 Steel

Both N08367 stainless steel and EN 1.0528 steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08367 stainless steel and the bottom bar is EN 1.0528 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
20
Fatigue Strength, MPa 280
180
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 490
320
Tensile Strength: Ultimate (UTS), MPa 740
520
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
48
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 33
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.4
Embodied Energy, MJ/kg 84
19
Embodied Water, L/kg 200
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
88
Resilience: Unit (Modulus of Resilience), kJ/m3 290
180
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0 to 0.030
0.27 to 0.34
Chromium (Cr), % 20 to 22
0 to 0.4
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
97.5 to 99.23
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 6.0 to 7.0
0 to 0.1
Nickel (Ni), % 23.5 to 25.5
0 to 0.4
Nitrogen (N), % 0.18 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.045