N08535 Stainless Steel vs. EN 1.0596 Steel

Both N08535 stainless steel and EN 1.0596 steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08535 stainless steel and the bottom bar is EN 1.0596 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
20
Fatigue Strength, MPa 220
230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
330
Tensile Strength: Ultimate (UTS), MPa 570
530
Tensile Strength: Yield (Proof), MPa 240
330

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
50
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 36
1.9
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
1.4
Embodied Energy, MJ/kg 87
19
Embodied Water, L/kg 230
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
93
Resilience: Unit (Modulus of Resilience), kJ/m3 140
290
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 3.3
14
Thermal Shock Resistance, points 13
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.24
Chromium (Cr), % 24 to 27
0
Copper (Cu), % 0 to 1.5
0 to 0.6
Iron (Fe), % 29.4 to 44.5
96.8 to 100
Manganese (Mn), % 0 to 1.0
0 to 1.7
Molybdenum (Mo), % 2.5 to 4.0
0
Nickel (Ni), % 29 to 36.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.035