N08535 Stainless Steel vs. EN 1.4592 Stainless Steel

Both N08535 stainless steel and EN 1.4592 stainless steel are iron alloys. They have 66% of their average alloy composition in common.

For each property being compared, the top bar is N08535 stainless steel and the bottom bar is EN 1.4592 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 46
23
Fatigue Strength, MPa 220
340
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
82
Shear Strength, MPa 400
400
Tensile Strength: Ultimate (UTS), MPa 570
630
Tensile Strength: Yield (Proof), MPa 240
500

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Maximum Temperature: Corrosion, °C 450
550
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 36
18
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 6.3
3.8
Embodied Energy, MJ/kg 87
52
Embodied Water, L/kg 230
180

Common Calculations

PREN (Pitting Resistance) 36
43
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
610
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 20
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 3.3
4.6
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.025
Chromium (Cr), % 24 to 27
28 to 30
Copper (Cu), % 0 to 1.5
0
Iron (Fe), % 29.4 to 44.5
62.6 to 68.4
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 2.5 to 4.0
3.5 to 4.5
Nickel (Ni), % 29 to 36.5
0
Nitrogen (N), % 0
0 to 0.045
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0.15 to 0.8