N08535 Stainless Steel vs. EN 1.7367 Steel

Both N08535 stainless steel and EN 1.7367 steel are iron alloys. They have 48% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08535 stainless steel and the bottom bar is EN 1.7367 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
18
Fatigue Strength, MPa 220
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
75
Tensile Strength: Ultimate (UTS), MPa 570
670
Tensile Strength: Yield (Proof), MPa 240
460

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Mechanical, °C 1100
600
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 13
26
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 36
7.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
2.6
Embodied Energy, MJ/kg 87
37
Embodied Water, L/kg 230
88

Common Calculations

PREN (Pitting Resistance) 36
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
560
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
24
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 3.3
6.9
Thermal Shock Resistance, points 13
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0 to 0.030
0.080 to 0.12
Chromium (Cr), % 24 to 27
8.0 to 9.5
Copper (Cu), % 0 to 1.5
0
Iron (Fe), % 29.4 to 44.5
87.3 to 90.3
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 2.5 to 4.0
0.85 to 1.1
Nickel (Ni), % 29 to 36.5
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0.2 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010