N08800 Stainless Steel vs. EN 1.5503 Steel

Both N08800 stainless steel and EN 1.5503 steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08800 stainless steel and the bottom bar is EN 1.5503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 4.5 to 34
12 to 17
Fatigue Strength, MPa 150 to 390
180 to 280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 340 to 580
270 to 320
Tensile Strength: Ultimate (UTS), MPa 500 to 1000
400 to 520
Tensile Strength: Yield (Proof), MPa 190 to 830
270 to 430

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 30
1.8
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.3
1.4
Embodied Energy, MJ/kg 76
18
Embodied Water, L/kg 200
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 42 to 160
41 to 81
Resilience: Unit (Modulus of Resilience), kJ/m3 96 to 1740
200 to 490
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 18 to 35
14 to 19
Strength to Weight: Bending, points 18 to 28
15 to 18
Thermal Diffusivity, mm2/s 3.0
14
Thermal Shock Resistance, points 13 to 25
12 to 15

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.1
0.16 to 0.2
Chromium (Cr), % 19 to 23
0
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 39.5 to 50.7
98.4 to 99.239
Manganese (Mn), % 0 to 1.5
0.6 to 0.8
Nickel (Ni), % 30 to 35
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025
Titanium (Ti), % 0.15 to 0.6
0

Comparable Variants