N08800 Stainless Steel vs. SAE-AISI A10 Steel

Both N08800 stainless steel and SAE-AISI A10 steel are iron alloys. They have 48% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is N08800 stainless steel and the bottom bar is SAE-AISI A10 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
72
Tensile Strength: Ultimate (UTS), MPa 500 to 1000
810 to 2040

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
40
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 30
5.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.3
2.1
Embodied Energy, MJ/kg 76
27
Embodied Water, L/kg 200
56

Common Calculations

PREN (Pitting Resistance) 21
5.1
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 18 to 35
29 to 73
Strength to Weight: Bending, points 18 to 28
25 to 46
Thermal Diffusivity, mm2/s 3.0
11
Thermal Shock Resistance, points 13 to 25
27 to 68

Alloy Composition

Aluminum (Al), % 0.15 to 0.6
0
Carbon (C), % 0 to 0.1
1.3 to 1.5
Chromium (Cr), % 19 to 23
0
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 39.5 to 50.7
90.8 to 93.4
Manganese (Mn), % 0 to 1.5
1.6 to 2.1
Molybdenum (Mo), % 0
1.3 to 1.8
Nickel (Ni), % 30 to 35
1.6 to 2.1
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
1.0 to 1.5
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0.15 to 0.6
0

Comparable Variants