N08800 Stainless Steel vs. N07041 Nickel
N08800 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is N08800 stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 4.5 to 34 | |
| 14 |
| Fatigue Strength, MPa | 150 to 390 | |
| 540 |
| Shear Strength, MPa | 340 to 580 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1000 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 190 to 830 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1360 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 12 | |
| 11 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 42 to 160 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 96 to 1740 | |
| 2510 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 18 to 35 | |
| 47 |
| Strength to Weight: Bending, points | 18 to 28 | |
| 34 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 3.0 |
| Thermal Shock Resistance, points | 13 to 25 | |
| 38 |