N08801 Stainless Steel vs. S39274 Stainless Steel

Both N08801 stainless steel and S39274 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08801 stainless steel and the bottom bar is S39274 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
17
Fatigue Strength, MPa 260
380
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
81
Shear Strength, MPa 570
560
Tensile Strength: Ultimate (UTS), MPa 860
900
Tensile Strength: Yield (Proof), MPa 190
620

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 630
450
Maximum Temperature: Mechanical, °C 1090
1100
Melting Completion (Liquidus), °C 1390
1480
Melting Onset (Solidus), °C 1360
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 30
24
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 5.5
4.3
Embodied Energy, MJ/kg 79
60
Embodied Water, L/kg 200
180

Common Calculations

PREN (Pitting Resistance) 21
43
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
140
Resilience: Unit (Modulus of Resilience), kJ/m3 92
940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 30
32
Strength to Weight: Bending, points 25
26
Thermal Diffusivity, mm2/s 3.3
4.2
Thermal Shock Resistance, points 20
25

Alloy Composition

Carbon (C), % 0 to 0.1
0 to 0.030
Chromium (Cr), % 19 to 22
24 to 26
Copper (Cu), % 0 to 0.5
0.2 to 0.8
Iron (Fe), % 39.5 to 50.3
57 to 65.6
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 0
2.5 to 3.5
Nickel (Ni), % 30 to 34
6.0 to 8.0
Nitrogen (N), % 0
0.24 to 0.32
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0.75 to 1.5
0
Tungsten (W), % 0
1.5 to 2.5