N08904 Stainless Steel vs. EN 1.4541 Stainless Steel

Both N08904 stainless steel and EN 1.4541 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is N08904 stainless steel and the bottom bar is EN 1.4541 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
190 to 270
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 38
14 to 40
Fatigue Strength, MPa 200
190 to 330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Shear Strength, MPa 370
410 to 550
Tensile Strength: Ultimate (UTS), MPa 540
600 to 900
Tensile Strength: Yield (Proof), MPa 240
220 to 570

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 430
480
Maximum Temperature: Mechanical, °C 1100
940
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 32
16
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
3.2
Embodied Energy, MJ/kg 79
46
Embodied Water, L/kg 200
140

Common Calculations

PREN (Pitting Resistance) 37
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 150
120 to 830
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
21 to 32
Strength to Weight: Bending, points 18
20 to 27
Thermal Diffusivity, mm2/s 3.1
4.0
Thermal Shock Resistance, points 12
14 to 20

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.080
Chromium (Cr), % 19 to 23
17 to 19
Copper (Cu), % 1.0 to 2.0
0
Iron (Fe), % 38.8 to 53
65.2 to 74
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 23 to 28
9.0 to 12
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.015
Titanium (Ti), % 0
0 to 0.7