N08904 Stainless Steel vs. SAE-AISI 4028 Steel

Both N08904 stainless steel and SAE-AISI 4028 steel are iron alloys. They have 47% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08904 stainless steel and the bottom bar is SAE-AISI 4028 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170
150 to 190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 38
14 to 23
Fatigue Strength, MPa 200
180 to 330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Shear Strength, MPa 370
310 to 380
Tensile Strength: Ultimate (UTS), MPa 540
490 to 630
Tensile Strength: Yield (Proof), MPa 240
260 to 520

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 32
2.1
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
1.5
Embodied Energy, MJ/kg 79
19
Embodied Water, L/kg 200
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
81 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 150
180 to 720
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
17 to 22
Strength to Weight: Bending, points 18
18 to 21
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 12
16 to 20

Alloy Composition

Carbon (C), % 0 to 0.020
0.25 to 0.3
Chromium (Cr), % 19 to 23
0
Copper (Cu), % 1.0 to 2.0
0
Iron (Fe), % 38.8 to 53
98.1 to 98.7
Manganese (Mn), % 0 to 2.0
0.7 to 0.9
Molybdenum (Mo), % 4.0 to 5.0
0.2 to 0.3
Nickel (Ni), % 23 to 28
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.035
0.035 to 0.050