N08926 Stainless Steel vs. Grade 8 Babbitt Metal

N08926 stainless steel belongs to the iron alloys classification, while grade 8 Babbitt Metal belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is N08926 stainless steel and the bottom bar is grade 8 Babbitt Metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
24
Poisson's Ratio 0.28
0.41
Shear Modulus, GPa 80
8.5
Tensile Strength: Yield (Proof), MPa 330
23

Thermal Properties

Latent Heat of Fusion, J/g 300
46
Melting Completion (Liquidus), °C 1460
270
Melting Onset (Solidus), °C 1410
240
Specific Heat Capacity, J/kg-K 460
150
Thermal Conductivity, W/m-K 12
24
Thermal Expansion, µm/m-K 16
24

Otherwise Unclassified Properties

Base Metal Price, % relative 33
19
Density, g/cm3 8.1
10
Embodied Carbon, kg CO2/kg material 6.2
3.9
Embodied Energy, MJ/kg 84
53
Embodied Water, L/kg 200
840

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 270
11
Stiffness to Weight: Axial, points 14
1.3
Stiffness to Weight: Bending, points 24
9.2
Thermal Diffusivity, mm2/s 3.2
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
14 to 16
Arsenic (As), % 0
0.3 to 0.6
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.050
Carbon (C), % 0 to 0.020
0
Chromium (Cr), % 19 to 21
0
Copper (Cu), % 0.5 to 1.5
0 to 0.5
Iron (Fe), % 41.7 to 50.4
0 to 0.1
Lead (Pb), % 0
77.1 to 81.2
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0.15 to 0.25
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
4.5 to 5.5
Zinc (Zn), % 0
0 to 0.0050