N09777 Nickel vs. ASTM A372 Grade L Steel
N09777 nickel belongs to the nickel alloys classification, while ASTM A372 grade L steel belongs to the iron alloys. They have 42% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is N09777 nickel and the bottom bar is ASTM A372 grade L steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 39 | |
| 14 |
| Fatigue Strength, MPa | 190 | |
| 670 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Shear Strength, MPa | 400 | |
| 700 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 1160 |
| Tensile Strength: Yield (Proof), MPa | 240 | |
| 1040 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 960 | |
| 430 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1390 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 3.5 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 1.7 |
| Embodied Energy, MJ/kg | 100 | |
| 22 |
| Embodied Water, L/kg | 200 | |
| 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 2890 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 | |
| 41 |
| Strength to Weight: Bending, points | 19 | |
| 31 |
| Thermal Shock Resistance, points | 16 | |
| 34 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.38 to 0.43 |
| Chromium (Cr), % | 14 to 19 | |
| 0.7 to 0.9 |
| Iron (Fe), % | 28.5 to 47.5 | |
| 95.2 to 96.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.8 |
| Molybdenum (Mo), % | 2.5 to 5.5 | |
| 0.2 to 0.3 |
| Nickel (Ni), % | 34 to 42 | |
| 1.7 to 2.0 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |
| Titanium (Ti), % | 2.0 to 3.0 | |
| 0 |