N09777 Nickel vs. SAE-AISI A3 Steel
N09777 nickel belongs to the nickel alloys classification, while SAE-AISI A3 steel belongs to the iron alloys. They have 45% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is N09777 nickel and the bottom bar is SAE-AISI A3 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 700 to 2150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 260 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1450 |
| Melting Onset (Solidus), °C | 1390 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 6.0 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 4.4 |
| Embodied Energy, MJ/kg | 100 | |
| 67 |
| Embodied Water, L/kg | 200 | |
| 78 |
Common Calculations
| PREN (Pitting Resistance) | 30 | |
| 8.9 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 25 to 77 |
| Strength to Weight: Bending, points | 19 | |
| 23 to 48 |
| Thermal Shock Resistance, points | 16 | |
| 23 to 70 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.35 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 1.2 to 1.3 |
| Chromium (Cr), % | 14 to 19 | |
| 4.8 to 5.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 28.5 to 47.5 | |
| 88.7 to 92 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.4 to 0.6 |
| Molybdenum (Mo), % | 2.5 to 5.5 | |
| 0.9 to 1.4 |
| Nickel (Ni), % | 34 to 42 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 2.0 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.8 to 1.4 |