N10001 Nickel vs. SAE-AISI M2 Steel

N10001 nickel belongs to the nickel alloys classification, while SAE-AISI M2 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is N10001 nickel and the bottom bar is SAE-AISI M2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 84
77
Tensile Strength: Ultimate (UTS), MPa 780
760 to 2150

Thermal Properties

Latent Heat of Fusion, J/g 320
260
Melting Completion (Liquidus), °C 1620
1610
Melting Onset (Solidus), °C 1570
1570
Specific Heat Capacity, J/kg-K 390
440
Thermal Expansion, µm/m-K 10
10

Otherwise Unclassified Properties

Base Metal Price, % relative 75
24
Density, g/cm3 9.2
8.4
Embodied Carbon, kg CO2/kg material 15
8.8
Embodied Energy, MJ/kg 200
130
Embodied Water, L/kg 260
98

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 22
23
Strength to Weight: Axial, points 24
25 to 71
Strength to Weight: Bending, points 21
22 to 44
Thermal Shock Resistance, points 25
27 to 76

Alloy Composition

Carbon (C), % 0 to 0.050
0.78 to 1.1
Chromium (Cr), % 0 to 1.0
3.8 to 4.5
Cobalt (Co), % 0 to 2.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 4.0 to 6.0
78.5 to 83.4
Manganese (Mn), % 0 to 1.0
0.15 to 0.4
Molybdenum (Mo), % 26 to 30
4.5 to 5.5
Nickel (Ni), % 58 to 69.8
0 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.2 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0
5.5 to 6.8
Vanadium (V), % 0.2 to 0.4
1.8 to 2.2